<p><strong>1.1 </strong>This part of ISO 9327 applies to forgings and rolled or forged bars in thicknesses up to 250 mm (partly up to</p>
<p>500 mm) manufactured from the steels listed in Table 1 and to be delivered according to the specifications given in</p>
<p>ISO 9327-1.</p>
<p><strong>1.2 </strong>This part of ISO 9327 covers the following data:</p>
<p>a) in Table 1 the limits for</p>
<p>the chemical composition according to the cast analysis;</p>
<p>the tensile properties at room temperature;</p>
<p>the impact properties;</p>
<p>the indications on the usual heat treatment condition at the time of delivery;</p>
<p>b) in Table 2 the permissible product analysis tolerances on the limiting values given for the cast analysis;</p>
<p>c) in Table 3 the minimum elevated temperature proof strength values (see C.4 of ISO 9327-1:1998);</p>
<p>d) in Table 4 the estimated average stress rupture properties;</p>
<p>e) in Table 5 the estimated average strength values for 1 % plastic strain.</p>
Reģistrācijas numurs (WIID)
89429
Darbības sfēra
<p><strong>1.1 </strong>This part of ISO 9327 applies to forgings and rolled or forged bars in thicknesses up to 250 mm (partly up to</p>
<p>500 mm) manufactured from the steels listed in Table 1 and to be delivered according to the specifications given in</p>
<p>ISO 9327-1.</p>
<p><strong>1.2 </strong>This part of ISO 9327 covers the following data:</p>
<p>a) in Table 1 the limits for</p>
<p>the chemical composition according to the cast analysis;</p>
<p>the tensile properties at room temperature;</p>
<p>the impact properties;</p>
<p>the indications on the usual heat treatment condition at the time of delivery;</p>
<p>b) in Table 2 the permissible product analysis tolerances on the limiting values given for the cast analysis;</p>
<p>c) in Table 3 the minimum elevated temperature proof strength values (see C.4 of ISO 9327-1:1998);</p>
<p>d) in Table 4 the estimated average stress rupture properties;</p>
<p>e) in Table 5 the estimated average strength values for 1 % plastic strain.</p>