<p>ISO 16701:2003 defines an accelerated corrosion test method to be used in assessing the corrosion resistance of metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or road de-icing salt.</p>
<p>ISO 16701:2003 specifies the test apparatus and test procedure to be used in conducting the accelerated corrosion test to simulate, in a very controlled way, atmospheric corrosion conditions.</p>
<p>In this International Standard, the term "metal" includes metallic materials with or without corrosion protection.</p>
<p>The accelerated laboratory corrosion test applies to</p>
<h3> metals and their alloys;</h3>
<h3> metallic coatings (anodic and cathodic);</h3>
<h3> chemical conversion coatings;</h3>
<h3> organic coatings on metals.</h3>
<p>The method is especially suitable for comparative testing in the optimization of surface treatment systems.</p>
Reģistrācijas numurs (WIID)
29388
Darbības sfēra
<p>ISO 16701:2003 defines an accelerated corrosion test method to be used in assessing the corrosion resistance of metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or road de-icing salt.</p>
<p>ISO 16701:2003 specifies the test apparatus and test procedure to be used in conducting the accelerated corrosion test to simulate, in a very controlled way, atmospheric corrosion conditions.</p>
<p>In this International Standard, the term "metal" includes metallic materials with or without corrosion protection.</p>
<p>The accelerated laboratory corrosion test applies to</p>
<h3> metals and their alloys;</h3>
<h3> metallic coatings (anodic and cathodic);</h3>
<h3> chemical conversion coatings;</h3>
<h3> organic coatings on metals.</h3>
<p>The method is especially suitable for comparative testing in the optimization of surface treatment systems.</p>